Abrasion Tester AT 100 XL (Bond Index)

Close

Language:


The Bond Abrasion Index, devised by F.C. Bond in the 1940‘s, quantifies the abrasivity of ores and minerals. The index serves to calculate metal wear rates in crushers and ball consumption rates in ball mills.

The AT 100 XL consists of a rotating insert into which dry ore samples with a defined particle size are placed. An impact paddle mounted on a centre shaft, rotating at a higher speed than the insert, grinds the sample over a defined period of time.

Both insert and paddle rotate in the same direction. The paddle is made from standard alloy steel hardened to 500 Brinell. The Abrasion Index is calculated from the weight loss of the paddle under standard operating conditions.

Fordeler

  • pre-set rotation speed and time
  • CE conform version

Egenskaper

funksjon quantification of the abrasivity of ores and minerals
bruksområde byggematerialer, geologi / metallurgi, miljø / gjenvinning
Evaluation calculation of loss of mass by weighing the paddle
størrelse på matematerialet* < 19 mm
prøvevolum* 400 g each process
Number of processes 4, each 400 g
Time for abrasivity test 4*15 min
Rotating paddle 3" x 1" x ¼" hardened to 500 Brinell
Rotating speed impact paddle 632 min-1 / insert 70 min-1
Elektriske tilkoblingsdata 230 V, 50 Hz
Nettilkobling 1-fase
b x h x d 700 x 1140 x 700 mm
nettovekt ~ 246 kg
Normer / standarer CE

Please note:
*avhengig av matemateriale og apparatkonfigurering /apparatinnstillinger

Virkemåte

The Bond Index Abrasion Tester AT 100 XL consists of a rotating insert into which a dry sample with a defined particle size is placed. An impact paddle mounted on a centre shaft rotating at a higher speed than the insert grinds the sample over a defined period of time.

Both insert and paddle rotate in the same direction. The paddle is made from standard alloy steel hardened to 500 Brinell. The Abrasion Index is calculated from the weight loss of the paddle under standard operating conditions.